分层对TC4钛合金板抗平头弹撞击失效特性的影响

摘要
图/表
参考文献(17)
相关文章 (15)

全文: PDF (1615 KB) HTML (1 KB)
输出: BibTeX | EndNote (RIS)

摘要

使用Abaqus/Explicit有限元分析软件，开展平头弹撞击不同厚度双层TC4钛合金板数值模拟，研究双层TC4钛合金板撞击失效特性与失效模式随厚度变化规律及机理。通过对比撞击试验与仿真结果，验证数值模型和参数的有效性。在此基础上与等厚度单层TC4钛合金板的抗侵彻性能进行对比，结果表明，对于12.68 mm直径的平头弹，在靶板厚度2～16 mm内，双层结构的弹道极限与总厚度近似呈线性关系。由于单层靶板在4～10 mm内随着厚度增加，弹道极限无明显变化，所以等厚接触式双层结构在该厚度范围相比单层靶有明显的优势。在总厚度为8 mm时，双层靶优势最为明显，弹道极限相比单层靶提高了43%左右。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	魏刚1
	冯岩1
	张铁纯1
	邓云飞1
	杨永刚2

关键词 ：撞击, 双层靶, 数值模拟, 弹道极限

Abstract：The finite element analysis software Abaqus/explicit was used to simulate the impact of flat nosed projectile on TC4 titanium alloy plates with different thickness. The relationship was studied between impact failure characteristics and thickness change of double-layer targets. The effectiveness of the simulation model was verified by comparing the impact tests and simulation results. On this basis, the penetration resistance of a TC4 double-layer target was compared with the same thickness of a monolithic target. The results show that the ballistic limit of the double-layer structure is approximately linear with the total thickness of the target plate in the range of 2-16 mm for the flat nosed projectile with 12.68 mm diameter. Due to the special phenomenon that the ballistic limit has no obvious change with the increase of the thickness for the monolithic target plate in the range of 4-10 mm, the double-layer target has obvious advantages over the monolithic target in the thickness range. The ballistic limit is 43% higher than that of the monolithic target when the total thickness is 8 mm.

Key words： impact double-layer targets numerical simulation ballistic limit

收稿日期: 2020-07-23 出版日期: 2021-04-28

引用本文:

魏刚1，冯岩1，张铁纯1，邓云飞1，杨永刚2. 分层对TC4钛合金板抗平头弹撞击失效特性的影响[J]. 振动与冲击, 2021, 40(8): 223-229.
WEI Gang1, FENG Yan1, ZHANG Tiechun1, DENG Yunfei1, YANG Yonggang2. Influence of the layering on the impact failure characteristics of a TC4 titanium target against blunt nose projectile impact. JOURNAL OF VIBRATION AND SHOCK, 2021, 40(8): 223-229.

链接本文:

http://jvs.sjtu.edu.cn/CN/ 或 http://jvs.sjtu.edu.cn/CN/Y2021/V40/I8/223

［1］郝鹏, 卿光辉, 李建峰,等. 2A12铝合金薄板对卵形头弹抗冲击性能研究［J］.振动与冲击,2016,35(17):19-25.
HAO Peng, QING Guanghui, LI Jianfeng, et al. Ballistic resistance of 2A12 thin plates against ogival-nosed projectiles impact［J］. Journal of Vibration and Shock, 2016, 35(17):19-25.
［2］DEY S, BRVIK T, TENG X, et al. On the ballistic resistance of double-layered steel plates: an experimental and numerical investigation［J］. International Journal of Solids and Structures, 2007, 44(20):6701-6723.
［3］GUPTA N K, IQBAL M A, SEKHON G S. Effect of projectile nose shape, impact velocity and target thickness on deformation behavior of aluminum plates［J］. International Journal of Impact Engineering, 2008, 44(10):3411-3439.
［4］NIA A A, HOSEINI G R. Experimental study of perforation of multi-layered targets by hemispherical-nosed projectiles［J］. Materials & Design, 2011, 32(2):1057-1065.
［5］任善良, 文鹤鸣, 周琳. 平头弹穿透接触式双层金属板的理论研究［J］. 高压物理学报, 2018, 32(3):87-93.
REN Shanliang, WEN Heming, ZHOU Lin. Theoretical study of the perforation of double-layered metal targets without spacing struckby flat-ended projectiles［J］. Chinese Journal of High Pressure Physics, 2018, 32(3): 87-93.
［6］RADIN J, GOLDSMITH W. Normal projectile penetration and perforation of layered targets［J］. International Journal of Impact Engineering, 1988, 7(2):229-259.
［7］CORRAN R S J, SHADBOLT P J, RUIZ C. Impact loading of plates:an experimental investigation［J］. International Journal of Impact Engineering, 1983, 1(1):3-22.
［8］李金福,智小琦,郝春杰,等.Q235钢靶分层结构抗异形破片侵彻性能研究［J］.弹箭与制导学报,2020,40(4):55-60.
LI Jinfu, ZHI Xiaoqi, HAO Chunjie, et al. Study on penetration performance of layered structure of Q235 steel targetagainst special fragments［J］. Journal of Projectiles, Rockets, Missiles and Guidance,2020,40(4):55-60.
［9］ZHANG W, DENG Y F, CAO Z S, et al. Experimental investigation on the ballistic performance of monolithic and layered metal plates subjected to impact by blunt rigid projectiles［J］. International Journal of Impact Engineering, 2012,49:115-129.
［10］惠旭龙, 刘小川, 王计真, 等. TC4钛合金平板高速撞击损伤及弹道极限特性［J］. 科学技术与工程, 2017,17(11):6-13.
HUI Xulong, LIU Xiaochuan, WANG Jizhen, et al. High velocity impact failure and ballistic performance of TC4 plate［J］. Science Technology and Engineering, 2017, 17(11):6-13.
［11］BRVIK T, HOPPERSTAD O S, LANGSETH M, et al. Effect of target thickness in blunt projectile penetration of Weldox 460 E steel plates［J］. International Journal of Impact Engineering, 2003, 28(4):413-464.
［12］张铁纯, 张永, 田锐, 等. TC4钛合金板厚度对其撞击失效特性影响研究［J］. 振动与冲击, 2020,39(10):52-57.
ZHANG Tiechun，ZHANG Yong，TIAN Rui, et al. Influence of the thickness on the impact failure characteristics of TC4 titanium alloy plate［J］. Journal of Vibration and Shock, 2020,39(10): 52-57.
［13］XIAO X K, MU Z C, HAO P, et al. Effect of the Lode parameter in predictingshear cracking of 2024-T351 aluminum alloy Taylor rods［J］. International Journal of Impact Engineering, 2018, 120:185-201.
［14］HANCOCK J W, MACKENZIE A C. On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress states［J］. Journal of the Mechanics and Physics of Solids,1976, 24:147-160.
［15］RECHT R F, IPSON T W. Ballistic perforation dynamics［J］. Journal of Applied Mechanics, 1963, 30(3):384-390.
［16］陈小伟, 梁冠军, 姚勇, 等, 平头弹穿透金属靶板的模式分析［J］. 力学学报, 2009, 41(1):84-90.
CHEN Xiaowei,LIANG Guanjun,YAO Yong,et al. Perforation modes of metal plates struck by a blunt rigid projectile［J］. Chinese Journal of Theoretical and Applied Mechanics, 2009, 41(1):84-90.
［17］邓云飞, 孟凡柱, 李剑锋,等. Q235钢板对半球形头弹抗侵彻特性［J］. 爆炸与冲击, 2015,35(3):386-392.
DENG Yunfei, MENG Fanzhu, LI Jianfeng, et al. The ballistic performance of Q235 metal plates subjected to impact by hemispherically-nosed projectiles［J］. Explosion and Shock Waves, 2015, 35(3):386-392.