Experimental study on the property deterioration of rubber material used as natural rubber bearing under seawater wet-dry cycles
LI Yanmin1，MA Yuhong1，ZHAO Guifeng2，ZHOU Fulin2
1.Earthquake Engineering Research & Test Center, Guangzhou University, Guangzhou 510405, China;
2. School of Civil Engineering, Guangzhou University, Guangzhou 510006, China;
Abstract：Considering that offshore bridges are highly vulnerable to seawater wet-dry cycles caused by the weather of sunny or rainy, high humidity, high temperature, sea breeze et al., seawater wet-dry cycles tests were carried out on a natural rubber bearing and its rubber material for 60 days to investigate the mechanical properties deterioration of rubber material with the test time.The results show: the seawater wet-dry cycles have a greater influence on the mechanical property of rubber material.After testing for 60 days, the hardness of rubber material increases by about 22%, the strain stress under given elongation increases from 58.2%—118% and the rate of increase is even greater in large deformation.The tensile strength and elongation at break reduce by 65.7% and 51.53% respectively, which may affect the tensile property and ultimate shear property of the rubber bearing.The study can lay a solid foundation for the research on the variation of the constitutive relationship for rubber material, the performance deterioration of rubber bearings, the evaluation of life cycle performance and the design of isolation projects.
李艳敏1，马玉宏1，赵桂峰2，周福霖2. 海水干湿循环作用下天然橡胶支座橡胶材料性能劣化试验[J]. 振动与冲击, 2019, 38(14): 146-152.
LI Yanmin1，MA Yuhong1，ZHAO Guifeng2，ZHOU Fulin2. Experimental study on the property deterioration of rubber material used as natural rubber bearing under seawater wet-dry cycles. JOURNAL OF VIBRATION AND SHOCK, 2019, 38(14): 146-152.
[1] Roberts, A.D. Natural rubber science and technology, Oxford University Press, UK, 1988.
[2] Hamed, G.R. Engineering with rubber materials and compounds, Hanser Publishers, Munich, 1992.
[3] Shelton, J.R. Review of basic oxidation processes in elastomers[J]. Rubber Chemistry and Technology, 1972,45: 359.
[4] Woo, C.S., Choi, B.I., Park, H.S., Kim, H.S. and Noh, H.B. Reliability evaluation of rubber mount for elevator cabin[J]. KGK-Kautschuk Gummi Kunststoffe, 2009,62(7-8):392–395.
[5] H.S.Gu and Y. Itoh. Ageing behaviour of natural rubber and high damping rubber material used in bridge rubber bearings[J]. Advances in Structural Engineering, 2010,13(6) :1105-1113.
[6] Abmalek K, Stevenson A. The effect of 42 year immersion in sea-water on natural rubber[J]. Journal of Materials Science,1986,(21):147-154．
[7] Mott P H, Roland C M．Aging of natural rubber in air and seawater[J]. Rubber Chemistry and Technology, 2001, 74(1) : 79 - 88．
[8] 余超, 文庆珍, 朱金华等. 特种氯丁橡胶在热空气及热海水中的老化与使用寿命预测[J]. 高分子材料科学与工程，2011,(4) : 37 -39.
Chao Yu, Qingzhen Wen, Jinhua Zhu et al. Aging in Sea Water and in Hot Air and Service Life Prediction of Neoprene[J]. Polymer Materials Science and Engineering, 2011, 74(1):79-88.
[9] 游海军. 模拟海洋环境下丁晴橡胶性能演变及寿命预测研究[D]. 青岛科技大学, 2016.
Haijun You. Study of performance evolution of nitrile rubber in marine environment and life prediction [D]. Qingdao University of Science & Technology, 2016.
[10] 马玉宏, 赵桂峰, 罗佳润等. 老化及海蚀作用下近海桥梁隔震支座橡胶材料性能劣化试验[J]. 振动与冲击, 2016, 35(16): 114-129.
Yuhong Ma, Guifeng Zhao, Jiarun Luo et al. Experimental research on property deterioration of rubber material used as natural rubber isolator for offshore bridges under aging and marine corrosion[J]. Journal of Vibration and Shock, 2016, 35(16):114-129.
[11] 赵建峰, 余超, 魏徵. 基于拉伸强度的特种氯丁橡胶使用寿命预测[J]. 弹性体, 2013,23(5):15-18.
Jianfeng Zhao, Chao Yu and Zheng Wei. Service life prediction for the neoprene base on tensile strength[J]. China Elastomerics, 2013, 23(5):15-18.
[12] 曹婷婷. 橡胶疲劳寿命的有限元分析研究[D]. 华南理工大学, 2014.
Tingting Cao. Finite element analysis of the fatigue life of rubber[D]. South China University of Technology, Guangzhou, China, 2014.
[13] Itoh.Y, Yazawa A, Kitagawa T， et al． Study on environmental durability of rubber bearing for bridges［ C］ / /IABSE Symposium Report． International Association for Bridge and Structural Engineering， 2002， 86 ( 11 ) : 137 －143．
[14] 刘建勋,黄友剑,刘柏兵等. 一种橡胶弹性元件疲劳寿命预测方法的研究[J]. 2011, 34(3):12-15.
Jianxun Liu, Youjian Huang, Baibing Liu et al. Research on fatigue life prediction method of rubber components[J]. Electric Locomotires & Mass Transit Vehicles, 2011, 34(3):12-15.
[15] 李昂. 橡胶的老化试验及老化变质程度的测定[J]．橡胶参考资料，2009, 39(4): 2－28.
Ang Li. Aging test of rubber and determination of aging metamorphism degree[J]. Rubber Reference，2009, 39( 4) :2－28．
[16] 张亚梅, 陈胜霞, 高岳毅. 浸-烘循环作用下橡胶水泥混凝土的性能研究[J]. 建筑材料 学报, 2005, 8(6): 665- 671.
Yamei Li, Shengxia Chen, Yueyi Gao. Study on properties of rubber included cement concrete under wet dry cycling[J]. Journal of Building Materials, 2005, 8(6):665-671.
[17] 王琴,杨鼎宜.干湿循环对混凝土硫酸盐侵蚀的影响[J]. 混凝土，2008,3：22-24.
Qin Wang, Dingyi Yang. Influence of the dry-wet circulation on the concrete sulfate attack[J]. Concrete, 2008, (3):22-24.
[18] 张峰,刘小燕,李术才. 海水侵蚀后混凝土三轴强度准则研究[J]. 工程力学,2010,27(9):209-215.
Feng Zhang, Xiaoyan Liu, Shucai Li. Research about triaxial strength criterion of concrete under sea water erosion environment[J]. Engineering Mechanics, 2010, 27(9):209-215.
[19] K．Hong, R.D. Hooton. Effects of cyclic chloride exposure on penetration of concrete cover[J].Cement and Concrete Research, 1999,29:1379-1386.
[20] B.J. Mohr, J.J. Biernacki and K.E. Kurtis. Microstructural and chemical effects of wet-dry cycling on pulp fiber cement composites[J]. Cement And Concrete Research, 2006,36(7): 1240- 1251.
[21] P. S. Mangat, Kribanandan Gurusamy Long term properties under marine exposure of fibre reinforced concrete containing PFA[J]. Materials andStructures,1988, 21(5):352-358.
[22] Alan. N Gent. Engineering with rubber how to design component 2nd edition[M]. Hanser Gardner Publications, 2001.
[23] P.K.弗雷克利,佩恩著,杜承泽等译. 橡胶在工程中应用的理论与实践[M]. 北京:化学工业出版社.1985.
P.K. Freakley, A.R.Payne and Translated by Chengzhe Du et al. Theory and practice of engineering with rubber[M]. Beijing: Chemical Industry Press, 1985.