| Ballistic performance and anti-ballistic mechanism of 6061 aluminum confined Al_2O_3 ceramic composite material#br# |
| HU Qin WANG Jinhua LV Juan XING Zhiyuan WU Yueyi |
| Ningbo Branch of Chinese Academy of Ordnance Science, Ningbo 315100, China |
|
|
|
|
Abstract A kind of metal-confined ceramic composite in which the matrix alloy is 6061 aluminum and the diameter of Al_2O_3 ceramic ball is 6 mm was fabricated by squeeze casting.The ballistic efficiency factor of the composite material was obtained through 12.7 mm and 30 mm armor piercing experiments and the anti-ballistic mechanism and damage mechanism were investigated.The results show that the mass efficiency of the metal-confined ceramic composite armors with average density about 3.3-3.4 g/cm3 resisting against 12.7 mm and 30 mm armor piercing bullets exceeds 2.2 and 1.7 respectively.A concentrated shock load on the surface of composite materials might be tranfered to a locally uniform load due to the impacts among ceramic balls.On the other hand, an array arranged alternately by flexible 6061 aluminum ball and hard Al_2O_3 ceramic ball in composite materials could disperse energy and increase the shock-wave reflection, resulting in the improvement of the ballistic performance of composite target.The energy absorbing mechanism reveals that the innovated armor is able to protect against projectiles, together with the benefit of weight saving.
|
|
Received: 27 April 2017
Published: 15 September 2018
|
|
|
|
[1] 蒋志钢，曾首义，申志强. 轻型陶瓷复合装甲结构研究进展[J]. 兵工学报，2010, 31(5):603-610.
JIANG Zhi-gang, ZENG Shou-yi, SHEN Zhi-qiang. Research progress on lightweight ceramic composite armor structure[J]. Acta Armamentarii, 2010, 31(5):603-610.
[2] 刘 薇，杨 军. 装甲防护材料的研究现状及发展趋势[J]. 材料热处理技术，2011, 40(2):108-111.
LIU Wei, YANG Jun. Current status and development of armor protective material[J]. Material & Heat Treatment, 2011, 40(2):108-111.
[3] 胡玉龙，蒋 凡. 装甲陶瓷的发展现状和趋势[J]. 兵器材料科学与工程，1996, 19(5):37-42.
HU Yu-long, JIANG Fan. Development and current status of armor ceramics[J]. Ordnance Material Science and Engineering, 1996, 19(5):37-42.
[4] Wang Q, Chen Z H, Chen Z F. Design and characteristics of hybrid composite armor subjected to projectile impact [J]. Materials and Design, 2013, 46:634-639.
[5] Zeng H B, Pattofatto S, Zhao H, et al. Perforation of sandwich plates with graded hollow sphere cores under impact loading[J]. International Journal of Impact Engineering, 2010, 11: 233-237.
[6] Jovicic J, Zavaliangos A, Ko F. Modeling of the ballistic behavior of gradient design composite armors [J]. Composites: Part A, 2000, 31: 773-784.
[7] 蒋宝权，李玉龙，刘元镛，等. SiC增强颗粒分布规律对梯度装甲板抗侵彻过程的影响[J]. 爆炸与冲击，2005, 25(6):493-498.
JIANG Bao-quan, LI Yu-long, LIU Yuan-yong, et al. Effects of SiC particle reinforcement distribution on the penetration of functionally graded armour[J]. Explosion and Shock Waves, 2005, 25(6):493-498.
[8] 刘桂武，倪长也，金 峰，等. 陶瓷/金属复合装甲抗弹约束效应述评[J]. 西安交通大学学报，2011, 45(3):7-24.
LIU Gui-wu, NI Chang-ye, JIN Feng, et al. Review of anti-ballistic confinement effects of ceramic-metal composite armor[J]. Journal of Xi’an Jiaotong University, 2011, 45(3):7-24.
[9] 晏麓晖，曾首义，蒋志刚，等. 陶瓷厚度与约束对陶瓷复合靶抗弹性能的影响[J]. 弹道学报，2009, 21(3):15-22.
YAN Lu-hui, ZENG Shou-yi, JIANG Zhi-gang, et al. Effects of ceramic thickness and confinement on performance of ceramic composite targets[J]. Journal of Ballistics, 2009, 21(3):15-22.
[10] Kim I K, WANG H, Weiss S J, et al. Embedded wideband metaresonator antenna on a high-impedance ground plane for vehicular applications [J]. IEEE Transaction on Vehicular Technology, 2012, 61(4):1665-1672.
[11] Chin E S. Army focused research team on functionally graded armor composites [J]. Material Science & Engineering A, 1999, 259:155-161.
[12] 侯海量，朱 锡，李 伟. 轻型陶瓷/金属复合装甲抗弹机理研究[J]. 兵工学报，2013, 34(1):105-114.
HOU Hai-liang, ZHU Xi, LI Wei. Investigation on bullet proof mechanism of light ceramic/steel composite armor[J]. Acta Armamentarii, 2013, 34(1):105-114.
[13] Shenllan D. Impact failure mechanisms in alumina tiles on finite thickness support and the effect of confinement [J]. International Journal of Impact Engineering, 2000, 24:313-328.
[14] 李 聪. 刚玉球/铝合金复合材料的制备及其抗弹性能研究[D]. 南京：南京航空航天大学，2008.
LI Cong. Studies on fabrication process and ballistic-resistance of corundum balls/aluminum alloy composites[D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2008.
[15] 郭 锐，南博华，周 昊，等. 点阵金属夹层结构抗侵彻试验研究[J]. 振动与冲击，2016, 35(24):45-50.
Guo Rui, Nan Bo-hua, Zhou Hao, et al. Experiment assessment of the ballistic response of a hybrid-cored sandwich structure[J]. Journal of vibration and shock, 2016, 35(24):45-50.
|
|
|
|