Effect of the stress state on the numerical prediction of the ballistic resistance of thin 6061-T6 aluminum alloy targets against sphere projectile impacts
Xinke Xiao 1 Yaopei Wang2 Shuang Wang1 Wei Zhang3
1. Nanyang Institute of Technology, School of Civil Engineering, Nanyang 473004;
2. Nanyang Institute of Technology, School of Software, Nanyang 473004;
3. Harbin Institute of Technology, Harbin 150008
Abstract:Recent studies show that the ductile fracture of some metals may depend on not only the stress triaxiality but also the Lode parameter. Two ductile fracture criteria developed in recent publications incorporating the Lode parameter effect were implemented into ABAQUS and were employed in the numerical prediction of the fracture behavior and ballistic resistance of 1.6 mm thick 6061-T6 aluminum alloy targets under impacts of the 7.9 mm diameter steel ball. To reveal the effect of the stress state, FE calculations by using another two fracture criteria without incorporation of the Lode parameter were conducted. These predictions were compared with test results reported in the open literature. The present comparison study shows that the incorporation of the Lode parameter can improve the prediction on the fracture behavior and ballistic resistance of 6061-T6 aluminum alloy targets.
肖新科1,王要沛2,王爽1,张伟3. 应力状态在球形弹丸撞击6061-T6铝薄靶弹道行为数值预报中的作用[J]. 振动与冲击, 2015, 34(22): 87-91.
Xinke Xiao 1 Yaopei Wang2 Shuang Wang1 Wei Zhang3. Effect of the stress state on the numerical prediction of the ballistic resistance of thin 6061-T6 aluminum alloy targets against sphere projectile impacts. JOURNAL OF VIBRATION AND SHOCK, 2015, 34(22): 87-91.
[1] Xiao X, Zhang W, Wei G, et al. Experimental and numerical investigation on the deformation and failure behavior in the Taylor test[J]. Materials and Design, 2011, 32:2663-2674.
[2] Gilioli A, Manes A, Giglio M, et al. Predicting ballistic impact failure of aluminium 6061-T6 with the rate-independent Bao-Wierzbicki fracture mode[J]. International Journal of Impact Engineering, 2015, 76:207-220.
[3] Anderson Jr CE, Chocron IS, Nicholls AE. Damage Modeling for Taylor Impact Simulations[J]. Journal De Physique IV France, 2006, 134:331-337.
[4] 陈刚. 半穿甲战斗部弹体穿甲效应数值模拟与实验研究[D]. 绵阳:中国工程物理研究院, 2006年.
[5] Kane A, Børvik T, Hopperstad OS, et al. Finite Element Analysis of Plugging Failure in Steel Plates Struck by Blunt Projectiles[J]. Journal of Applied Mechanics, 2009, 76:051302-1-11.
[6] Bai Y, Wierzbicki T. A new model of metal plasticity and fracture with pressure and Lode dependence[J]. International Journal of Plasticity, 2008, 24:1071-1096.
[7] 张伟, 肖新科, 魏刚. 7A04铝合金的本构关系和失效模型[J]. 爆炸与冲击, 2011, 31:81-87.
ZHANG Wei, XIAO Xin-ke, WEI Gang. Constitutive relation and fracture model of 7A04 aluminum alloy[J]. EXPLOSION AND SHOCK WAVES, 2011, 31:81-87.
[8] Wierzbicki T, Bao Y, Lee YW, et al. Calibration and Evaluation of Seven Fracture Models[J]. International Journal of Mechanical Sciences, 2005, 47:719-743.
[9] 刘超, 孙秦, 刘彦杰, 等. 延性金属渐进破坏试验与数值研究[J]. 航空材料学报, 2013, 33:93-99.
LIU Chao, SUN Qin, LIU Yan-jie, et al. Experimental and Numerical Study of Progressive Failure of Ductile Metals[J]. JOURNAL OF AERONAUTICAL MATERIALS, 2013, 33:93-99.
[10] Chocron S, Erice B, Anderson CE. A new plasticity and failure model for ballistic application[J]. International Journal of Impact Engineering, 2011, 38:755-764.
[11] Lidén E, Mousavi S, Helte A, et al. Deformation and fracture of a long-rod projectile induced by an oblique moving plate: Numerical simulations[J]. International Journal of Impact Engineering, 2012, 40-41:35-45.
[12] Li B, Kidane A, Ravichandran G, et al. Verification and validation of the Optimal Transportation Meshfree(OTM) simulation of terminal ballistics[J]. International Journal of Impact Engineering, 2012, 42:25-36.
[13] Johnson GR, Cook WH. A Constitutive Model and Data for Metals Subjected to Large Strains, High Strain Rates and High Temperatures[C]. Proceeding of the Seventh International Symposium on Ballistic. The Netherlands: The Hague, 1983. 541-547.
[14] Manes A, Lumassi D, Giudici L, et al. An experimental–numerical investigation on aluminium tubes subjected to ballistic impact with soft core 7.62 ball projectiles[J]. Thin-Walled Structures, 2013, 73:68-80.
[15] Johnson GR, Cook WH. Fracture Characteristics of Three Metals Subjected to Various Strains, Strain Rates, Temperatures and Pressures[J]. Engineering Fracture Mechanics, 1985, 21:31-48.
[16] Bai Y, Wierzbicki T. Application of extended Mohr-Coulomb criterion to ductile fracture[J]. International Journal of Fracture, 2010, 161:1-20.
[17] Lesuer DR, Kay GJ, LeBlanc MM. Modeling large-strain, high rate deformation in metals[R]. UCRL-JC-134118. Livermore, CA 94550, United States of America: Lawrence Livermore National Laboratory, 2001.
[18] Lou Y, Yoon JW, Huh H. Modeling of shear ductile fracture considering a changeable cut-off value for stress triaxiality[J]. International Journal of Plasticity, 2014, 54:56-80.
[19] Recht RF, Ipson TW. Ballistic Perforation Dynamics[J]. Journal of Applied Mechanics-Transactions ASME, 1963, 30:385-391.
[20] 王仲仁, 胡卫龙, 胡蓝. 屈服准则与塑性应力-应变关系理论及应用[M].北京:高等教育出版社, 2014.
[21] Barsoum I, Faleskog J. Rupture mechanisms in combined tension and shear-Experiments. International Journal of Solids and Structures, 2007, 44:1768-1786.