It is meaningful to identify the threshold load generating the delamination growth in the determination of the impact energy causing the damage of composite laminates subjected to small mass impact.The simulation results based on the analytical model show that the contact force drops sharply when the local contact rigidity is decreased, while the decrease of flexural rigidity of the whole plate does not introduce this feature into the response.A tester for small mass impact was fabricated and the impact tests were conducted on the laminates with variant energies.The contact force was detected by measuring the impactor responses and the laminate deflection at the impact point.It is shown that the contact force drops sharply at the theoretical delamination threshold load once the significant delamination is generated, and then goes up again.This phenomenon can be employed to identify the growth of delamination during the impact.To capture the sudden drop of the contact force obtained from the plate deflection, the sampling rate should be no less than 200 kHz.Otherwise, one may lose the sudden drop instant of the contact force curve slope.
叶文勋,于哲峰. 复合材料层压板小质量冲击下分层扩展的接触力阈值识别[J]. 振动与冲击, 2018, 37(18): 145-151.
YE Wenxun, YU Zhefeng,. Identification of threshold load causing delamination growth in composite laminates subjected to small mass impact. JOURNAL OF VIBRATION AND SHOCK, 2018, 37(18): 145-151.
[1] Olsson R. Mass criterion for wave controlled impact response of composite plates [J].Composites Part A, 2000, 31(8): 879–887.
[2] ASTM D7136/D7136M-12, Standard test meth-od for measuring the damage resistance of a fiber reinforced polymer matrix composite to a drop weight impact event[S]. West Con-shohocken: American Society for Testing and Materials (ASTM), 2012.
[3] 罗靓, 张佐光, 李敏,等.复合材料层合板准静态压痕实验研究[J].复合材料学报, 2007, 24(3):154-159.
LUO Liang, ZHANG Zuoguang, LI Min, el al. Experimental study on quasi-static indentation damage resistance of composite laminates [J]. Acta Materiae Compositae Sinica, 2007, 24(3):154-159.
[4] 郑晓霞,郑锡涛,沈真,等.低速冲击与准静态压痕力下复合材料层压板的损伤等效性 [J]. 航空学报, 2010, 31(5):928-933.
ZHENG Xiaoxia1, ZHENG Xitao, SHEN Zhen, et al. Damage Equivalent of Composite Laminates Subjected to Drop-weight Impact and Quasi-static Indentation Force [J]. Acta Aeronautica Et Astronautica Sinica, 2010, 31(5):928-933.
[5] Askari A, Nelson K, Weckner O, et al. Hail im-pact characteristics of a hybrid material by ad-vanced analysis techniques and testing [J]. Journal of Aerospace Engineering, 2011, 24(2):210-217.
[6] Schoeppner G A, Abrate S. Delamination threshold loads for low velocity impact on com-posite laminates [J]. Composites Part A Applied Science & Manufacturing, 2000, 31(9): 903–915.
[7] 宁宝军, 于哲峰, 叶文勋, 等. 基于非接触位移测量的层压板低速冲击性能分析[J]. 复合材料学报, 2016, 33(7):1564-1573.
NING Baojun, YU zhefeng, Ye wenxun, et al.. Damage resistance analysis of composite laminates subjected to low velocity impact based on non-contact measurement displacement [J]. Acta Materiae Compositae Sinica, 2016, 33(7):1564-1573.
[8] Minnaar K, Zhou M. A novel technique for time-resolved detection and tracking of interfacial and matrix fracture in layered [J]. Journal of the Mechanics and Physics of Solids, 2004, 52(12): 2771 –2799.
[9] Singh, H. and Mahajan P. Analytical modeling of low velocity large mass impact on composite plate including damage evolution [J]. Composite Structures, 2016, 149: 79-92.
[10] 刘万雷,常新龙,张晓军,等. 基于改进Hashin准则的复合材料低速冲击损伤研究[J]. 振动与冲击 , 2016 , 35 (12) :209-214.
LIU Wanlei, CHANG Xinlong, ZHANG Xiaojun, et al. Low-velocity impact analysis of composite plates based on modified Hashin cri-terion [J]. Journal of Vibration and Shock, 2016, 35(12): 209-214.
[11] Davies G A O, Zhang X. Impact damage predic-tion in carbon composite structures [J]. Interna-tional Journal of Impact Engineering, 1995, 16(1):149-170.
[12] Sutherland L S, Soares C G. Contact indentation of marine composites [J]. Composite Structures, 2005, 70(3): 287-94.
[13] Olsson R, Donadon M V, Falzon B G. Delami-nation threshold load for dynamic impact on plates [J]. International Journal of Solids and Structures, 2006, 43(10):3124-3141.
[14] Olsson R. Analytical model for delamination growth during small mass impact on plates [J]. International Journal of Solids and Structures, 2010, 47(21): 2884-2892.
[15] 陈艳.小质量冲击下层压板分层响应特性与接触力测量方法数值模拟研究[D].上海:上海交通大学,2015.
CHEN Yan. Numerical study on delaminat-ing-response characteristics and contact force measurement of composite laminate subjected to small-mass impact. [D]. Shanghai: Shanghai Jiao Tong University, 2015.
[16] Olsson R. Impact response of orthotropic compo-site plates predicted from a one-parameter dif-ferential equation [J]. AIAA Journal, 1992, 30(6):1587-1596.
[17] Olsson R. Closed form prediction of peak load and delamination onset under small mass impact [J]. Composite Structures 2003, 59(3):340–348.
[18] Goldsmith W. Impact [M], Edward Arnold, London, 1960, IV: 82-144.
[19] Rechak S Effect of adhesive layers on impact damage and dynamic response in composite laminates [D]. Purdue University, West Lafayette, 1986.
[20] Wenxun Ye, Zhefeng Yu, Baojun Ning, et al. On the Contact Force Measurement for Small Mass Impact of Composite Laminate and the Delamination Event Identification [C]. 58th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference, Grapevine, Dallas, Texas, Jan 9-13 2017