Damage characteristics of T800-CFRP laminates under non-normal impact of ice balls and tungsten beads
SHANG Xiaozhuang1, LIU Yaolu1,2, FENG Xiaowei3, HU Ning1,4, TAN Xiaojun3, HU Yanhui3
1.College of Aerospace Engineering, Chongqing University, Chongqing 400044, China;
2.Chongqing Municipal Key Lab of Heterogeneous Material Mechanics, Chongqing University, Chongqing 400044, China;
3.Institute of Systems Engineering, China Academy of Engineering Physics, Mianyang 621900, China;
4.College of Mechanical Engineering, Hebei University of Technology, Tianjin 300401, China
Abstract：The damage characteristics of T800-CFRP laminates under non-normal impact of hail ices and wolfram balls were studied by experiments and simulations. Firstly, the experiments of the high-speed impact of hail ices and wolfram balls on T800-CFRP laminates under given working conditions were carried out to verify the effectiveness of the simulation model; and then the damage characteristics and theirs differences of T800-CFRP laminates impacted by two kinds of impact bodies with different impact energies and impact angles were discussed. Research results have shown that wolfram balls can cause the perforation damage to laminates when the impact energy is low, and the damage degree of the laminates decreases with the increase of the impact energy; the impact energy threshold of hail ices causing damage to laminates is much higher than that of wolfram balls, and the damage degree increases significantly with the increase of the impact energy; the damage caused by wolfram balls at the impact angles of 450 and 600 is much more serious than that caused by the normal impact, while the damage caused by the impact angle of 300 is less than that caused by the normal impact; the damage degree of the laminate decreases with the increase of the impact angle by hail ices. This study is helpful to deepen the understanding of the damage and failure behavior of T800-CFRP laminates under impact load, and has important scientific significance and engineering value.
尚晓壮1，刘瑶璐1,2，冯晓伟3，胡宁1,4，谭晓军3，胡艳辉3. 冰雹和钨珠非正冲击下T800-CFRP层合板损伤特性的研究[J]. 振动与冲击, 2024, 43(11): 135-147.
SHANG Xiaozhuang1, LIU Yaolu1,2, FENG Xiaowei3, HU Ning1,4, TAN Xiaojun3, HU Yanhui3. Damage characteristics of T800-CFRP laminates under non-normal impact of ice balls and tungsten beads. JOURNAL OF VIBRATION AND SHOCK, 2024, 43(11): 135-147.
[1] 贺福. 碳纤维复合材料在大飞机上的应用[J]. 高科技纤维与应用, 2007, 32(6): 5-9.
He Fu. The application of carbon fiber composite materials in giant plane[J]. Hi-Tech Fiber & Application, 2007, 32(6) : 5-9. (in Chinese)
[2] 沈真. 碳纤维复合材料在飞机结构中的应用[J]. 高科技纤维与应用, 2010, 35(4): 1-4.
Shen Zhen. Application of carbon fiber composites in aircraft sructures[J]. Hi-Tech Fiber & Application. (in Chinese)
[3] Kim H, Kedward K T. Modeling hail ice impacts and predicting impact damage initiation in composite structures [J]. Aiaa Journal, 2000, 38(7): 1278-1288.
[4] Tippmann J D, Kim H, Rhymer J D. Experimentally validated strain rate dependent material model for spherical ice impact simulation [J]. International Journal of Impact Engineering, 2013, 57: 43-54.
[5] 王计真. 复合材料层合板抗冰雹冲击性能研究[J]. 兵工学报, 2017, 38(S1): 89-95.
Wang Jizhen. Research on anti-hailstone impact behavior of laminated composite panel.[J], Acta armamentarii, 2017, 38(S1): 89-95. (in Chinese)
[6] Johnson A F, Holzapfel M. Numerical prediction of damage in composite structures from soft body impacts[J]. Journal of Materials Science, 2006, 41(20): 6622-6630.
[7] 胡宗文, 袁国青. 基于SPH模型的冰雹高速冲击复合材料结构响应规律研究[J]. 力学季刊, 2016, 37(01): 104-113.
Hu Zongwen, Yuan Guoqing. Response regularity of composite structures under high velocity hail impact based on SPH model[J].Chinese quarterly of mechanics, 2016, 37(01): 104-113. (in Chinese)
[8] 张卓. 基于光滑粒子法与有限元法耦合的鸟撞发动机叶片响应分析[D]; 南京：南京理工大学, 2019.
Zhang Zhuo. Response analysis of bird impact engine blade based on smoothed particle hydrodynamics method and finite element method coupling[D]. Nanjing: Nanjing University of Science & Technology, 2019. (in Chinese)
[9] Anghileri M, Castelletei L M L, Invernizzi F, et al. A survey of numerical models for hail impact analysis using explicit finite element codes[J]. International Journal of Impact Engineering, 2005, 31(8): 929-944.
[10] Cantwell W J, Morton J. The impact resistance of composite materials - A REVIEW[J]. Composites, 1991, 22(5): 347-362.
[11] Jordan J B, Naito C J. An experimental investigation of the effect of nose shape on fragments penetrating GFRP[J]. International Journal of Impact Engineering, 2014, 63(9): 63-71.
[12] 古兴瑾, 许希武. 不同形状弹体高速冲击下复合材料层板损伤分析[J]. 工程力学, 2013, 30(1): 432-440.
Gu Xingjin, Xu Xiwu. Analysis of damage in composite laminates under high velocity impact by projectiles of diferent shapes[J]. Engineering Mechanics, 2013, 30(1): 432-440. (in Chinese)
[13] Fujii K, Aoki M, Kiuch N, et al. Impact perforation behavior of CFRPs using high-velocity steel sphere[J]. International Journal of Impact Engineering, 2002, 27(5): 497-508.
[14] 邓云飞, 蔡雄峰, 曾宪智, 等. 弹体头部形状对碳纤维层合板抗冲击性能影响实验研究[J]. 振动与冲击, 2020, 39(07): 86-92.
Deng Yunfei, Cai Xiongfeng, Zeng Xianzhi, et al. Tests for effects of projectile nose shape on anti-impact performance of carbon fiber reinforced plates[J]. Journal of Vibration and Shock, 2020, 39(07): 86-92. (in Chinese)
[15] 古兴瑾, 许希武. 纤维增强复合材料层板高速冲击损伤数值模拟[J]. 复合材料学报, 2012, 29(01): 150-161.
Gu Xingjin, Xu Xiwu. Numerical simulation of damage in fiber reinforced composite laminates under high velocity impact[J]. Acta Materias Composite Sinica, 2012, 29(01): 150-161. (in Chinese)
[16] Lopez-puente J, Zaera R, Navarro C. Experimental and numerical analysis of normal and oblique ballistic impacts on thin carbon/epoxy woven laminates[J]. Composites Part A: Applied Science and Manufacturing, 2008, 39(2): 374-387.
[17] Pernas-sanchez J, Artero-guerrero J A, Varas D, et al. Experimental analysis of normal and oblique high velocity impacts on carbon/epoxy tape laminates [J]. Composites Part A: Applied Science and Manufacturing, 2014, 60: 24-31.
[18] 马凯, 许希武, 古兴瑾. 纤维增强复合材料层板高速倾斜冲击损伤数值模拟[J]. 复合材料学报, 2013, 30(03): 211-219.
Ma Kai, Xu Xiwu, Gu Xinjin. Numerical simulation of damage in fiber reinforce composite laminates under high velocity oblique impact[J]. .Acta Materias Composite Sinica, 2013, 30(03): 211-219. (in Chinese)
[19] 邓云飞, 袁家俊, 徐建新. 半球形头弹不同角度冲击下编织复合材料板的侵彻特性[J]. 复合材料学报, 2018, 35(04): 843-849.
Deng Yunfei, Yuan Jiajun, Xu Jianxin. Penetration characteristics of woven composite laminates impacted by hemispherical-nosed projectiles at different angles[J]. Acta Materias Composite Sinica, 2018, 35(04): 843-849. (in Chinese)
[20] Coles L A, Roy A, Silberschmidt V V. Ice vs. steel: Ballistic impact of woven carbon/epoxy composites. Part II-Numerical modelling[J]. Engineering Fracture Mechanics, 2020, 225.
[21] 周逃林. 层合复合材料冰雹和硬物冲击损伤研[D]; 南京：南京航空航天大学, 2019.
Zhou Taolin. Study on damage of composite laminate experienced impactions of hail and rigid impactor[D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2019. (in Chinese)
[22] 李厚伯. 冲击载荷作用下碳纤维增强复合材料层合板的动力学响应研究[D]. 重庆：重庆大学, 2021.
Li Houbo. Dynamic response of carbon fiber reinforced composite laminates according to impact load[D]. Chongqing: Chongqing University, 2021. (in Chinese)
[23] Xie W, Zhang W, Kuang N, et al. Experimental investigation of normal and oblique impacts on CFRPs by high velocity steel sphere[J]. Composites Part B: Engineering, 2016, 99(11): 483-493.
[24] Williams K V, Vaziri R, Poursartiop A. A physically based continuum damage mechanics model for thin laminated composite structures[J]. International Journal of Solids and Structures, 2003, 40(9): 2267-2300
[25] Rhymer J, Kim H, Roach D. The damage of quasi-isotropic carban/epoxy composite tape laminates impacted by high velocity ice[J]. Composites Part A: Applied Science and Manufacturing, 2012, 43(4): 1134-1144.
[26] 宋振华. 冰载荷作用下碳纤维复合材料桁条加筋曲面板的冲击动力响应研究[D]. 广州: 暨南大学, 2014.
Song Zhenhua. The dynamic response of stringer-stiffened curved composite panels underthe hail ice impact[D]. Guangzhou: Jinan University, 2014.