Experimental study on the seismic behaviors of wasted fiber recycled concrete frame joints

ZHOU Jinghai1,KANG Tianbei2,WANG Fengchi2,SHU Yuncong2#br# 

Author information +

文章历史 +

摘要

完成了再生骨料取代率为50%，废弃纤维长度分别为12mm、19mm、30mm以及废弃纤维体积掺量分别为0.08%、0.12%、0.16%的5个废弃纤维再生混凝土框架中柱节点在低周反复荷载作用下的抗震性能试验研究。主要对不同废弃纤维长度、不同废弃纤维体积掺量下梁柱节点的破坏形态、滞回特性、延性性能、耗能特性等问题进行了对比分析。结果表明：废弃纤维再生混凝土框架节点的破坏均经历了初裂、通裂、极限、破坏四个特征阶段，当纤维长度为19mm，废弃纤维体积掺量为0.12%时，废弃纤维再生混凝土梁柱节点构件的滞回性能、延性性能及耗能性能较好；废弃纤维的体积掺量比废弃纤维长度对梁柱节点抗震性能的影响大。提出了废弃纺织纤维再生混凝土的抗剪承载力计算公式，计算结果与试验结果吻合较好。

Abstract

The seismic behaviors of interior frame joints composed of wasted fiber recycled aggregate concrete were studied experimentally. The effects of certain design parameters such as the length and volume ratio of wasted fiber with a constant replacement rate of recycled aggregate on the anti-seismic performance of the frame were investigated,5 full-scale specimens were designed and fabricated,then cyclic loading tests were conducted. In the tests,the replacement rate of recycled aggregate was kept at 50%,the wasted fiber length was 12 mm,19 mm,30 mm and volume content was 0.08%,0.12% and 0.16% respectively. The failure mode,hysteretic property,ductility,energy dissipation characteristics and other issues of frame joints were analyzed with different wasted fiber lengths and volume contents. The experimental results show that the destruction of wasted fiber recycled concrete frame joints experience four stages,they are initial cracking,thorough cracking,ultimate stage and failure stage. With the fiber length of 19 mm and volume content of 0.12%,the wasted fiber recycled concrete beam-column joint has better seismic behaviors. Compared with the wasted fiber length,the volume of wasted fiber content has greater influence on the seismic performance of beam-column joints. A shear strength calculation formula for wasted fiber recycled aggregate concrete was put forward. The calculation results coincide well with the test results.

导出引用

周静海1，康天蓓2，王凤池2，舒云聪2. 废弃纤维再生混凝土框架中柱节点抗震性能试验研究[J]. 振动与冲击, 2017, 36(2): 235-242

ZHOU Jinghai1,KANG Tianbei2,WANG Fengchi2,SHU Yuncong2. Experimental study on the seismic behaviors of wasted fiber recycled concrete frame joints[J]. Journal of Vibration and Shock, 2017, 36(2): 235-242

参考文献

[1] 肖建庄. 再生混凝土[M]. 北京:中国建筑工业出版社, 2008.
   Xiao Jian-zhuang. Recycled concrete[M]. Beijing: Building Industry Press of China, 2008.
[2] 梁超锋, 刘铁军, 邹笃建, 等. 再生混凝土材料阻尼性能研究[J]. 振动与冲击, 2013, 32(9): 160-164.
   LIANG Chao-feng, LIU Tie-jun, ZOU Du-jian, et al. Damping capacity of recycled concrete[J]. Journal of Vibration and Shock, 2013, 32(9): 160-164.
[3] 陈宗平, 陈宇良, 姚侃. 再生混凝土三轴受压力学性能试验及其影响因素[J]. 建筑结构学报, 2014, 35(12): 73-80.
   CHEN Zong-ping, CHEN Yu-liang, YAO Kan. Experimental research on mechanical behavior and influence factor of recycled coarse aggregate concretes under tri-axial compression [J]. Journal of Building Structures, 2014, 35(12): 73-80.
[4] A. Domingo-Cabo, C. Lazaro, F. Lopez-Gayarre. Creep and shrinkage of recycled aggregate concrete [J]. Construction and Building Materials, 2009, 23(7):2545-2553.
[5] 周静海, 张东, 杨永生. 废弃纤维再生混凝土梁受弯性能试验[J]. 沈阳建筑大学学报(自然科学版), 2013, 29(2): 290-296.
   ZHOU Jing-hai, ZHANG Dong, YANG Yongsheng. Test study on flexural properties of waste fiber recycled concrete beams[J]. Journal of Shenyang Jianzhu University (Natural Science), 2013, 29(2): 290-296.
[6] Wang Kejin, Shah S P, Pariya P. Plastic shrinkage cracking in concrete materials influence of fly ash and fibers[J]. ACI Materials Journal, 2001, (6):458-464.
[7] Carneiro Jodilson Amorim, Lima Paulo Roberto Lopes, Leite Mônica Batista. Compressive stress-strain behavior of steel fiber
reinforced-recycled aggregate concrete[J]. Cement and Concrete Composites, 2014, 46: 65-72.
[8] 赵海龙, 王铁成, 郝津津, 等. 纤维增强钢筋混凝土T形柱框架边节点的抗震性能试验研究[J]. 建筑结构学报, 2014, 35(S1):10-15.
   ZHAO Hai-long, WANG Tie-cheng, HAO Jin-jin. Experimental investigation on seismic behavior of fiber reinforced exterior joints with T-shaped column[J]. Journal of Building Structures, 2014, 35(S1):10-15.
[9] 刘超, 白国良, 贾胜伟,等. 不同轴压比再生混凝土框架节点抗震性能试验研究[J]. 土木工程学报, 2013, 46(6)：21-23.
    LIU Chao, BAI Guo-liang, JIA Sheng-wei, et al. Experimental study on seismic behavior of recycled concrete frame joints with different axial compression ratios[J]. China Civil Engineering Journal, 2013, 46(6)：21-23.
[10] 肖建庄, 朱晓晖. 再生混凝土框架节点抗震性能研究[J]. 同济大学学报(自然科学版), 2005, 33(4):437-439.
    XIAO Jian-zhuang, ZHU Xiao-hui. Study on seismic behavior of recycled concrete frame joints[J]. Journal of TongJi University(Natural Science), 2005, 33(4):437-439.
[11] 刘炳康, 陈丽华, 周安, 等. 再生混凝土框架柱中节点抗震性能试验研究[J]. 建筑结构学报, 2011, 32(11):109-115.
    LIU Bing-kang, CHEN Li-hua, ZHOU An, et al. Experimental study on seismic behavior of recycled aggregate concrete beam-column interior-joints [J]. Journal of Building Structures, 2011, 32(11):109-115.
[12] 姚振纲, 刘祖华. 建筑结构试验[M]. 上海:同济大学出版社, 1996.
[13] GB 50011-2010, 建筑抗震设计规范[S]. 北京:中国建筑工业出版社, 2001.
[14] 唐九如.钢筋混凝土框架节点抗震[M].南京:东南大学出版社, 1989.
[15] 聂建国, 朱力, 樊健生, 等. 钢板剪力墙抗震性能试验研究[J]. 建筑结构学报, 2013, 34(1): 65-68.
    NIE Jian-guo, ZHU Li, FAN Jian-sheng, et al. Experimental research on seismic behavior of steel plate shear wall[J]. Journal of Building Structures, 2013, 34(1): 65-68.