高强38CrSi钢力学性能测试及本构关系研究

PDF(1354 KB)

振动与冲击 ›› 2019, Vol. 38 ›› Issue (18) : 179-184.

论文

魏刚 1，张伟 2，邓云飞 1

作者信息 +

Mechanical property tests and the constitutive relation of high strength 38CrSi steel

WEI Gang1,ZHANG Wei2,DENG Yunfei1

Author information +

文章历史 +

摘要

使用万能材料试验机、霍普金森拉杆（SHTB）和Taylor杆撞击试验研究了淬火加中温回火处理的高强38CrSi钢在常温~700 ℃的准静态、动态力学性能。基于试验数据，对Johnson-Cook（J-C）本构模型中的温度软化项做了轻微修改。结合Taylor杆撞击试验反算，得到了修改的J-C本构相关参数和Cockroft-Latham（C-L）断裂准则的模型参数。通过对高速下Taylor杆撞击试验中弹体变形和断裂的数值仿真与试验结果的比较，验证了模型及参数对预测高强38CrSi钢动态大变形和断裂的有效性。

Abstract

The quasi-static and dynamic mechanical behaviors of high strength 38CrSi steel with medium temperature tempering after quenching were investigated using a universal testing machine and a split Hopkinson tension bar (SHTB) for doing the Taylor impact test.The temperature range from room temperature to 700 °C was involved.The Johnson-Cook (J-C) constitutive relation with a slight modification on the temperature softening item was proposed to fit the test results.The modified parameters of the J-C constitutive model and Cockroft-Latham (C-L) fracture criterion were identified by fitting the experimental data, based on the combination of the numerical simulation results of Taylor impact test and the conditions of mushrooming and cracking.The parameters were validated by comparising the deformation and fracture results by the Taylor tests and the simulations with higher impact velocity.The consistency between experimental observations and numerical simulations indicates that the models and parameters obtained are competent to describe the dynamic large deformations and fracture behaviors of high strength 38CrSi steel.

导出引用

魏刚 1，张伟 2，邓云飞 1. 高强38CrSi钢力学性能测试及本构关系研究[J]. 振动与冲击, 2019, 38(18): 179-184

WEI Gang1,ZHANG Wei2,DENG Yunfei1. Mechanical property tests and the constitutive relation of high strength 38CrSi steel[J]. Journal of Vibration and Shock, 2019, 38(18): 179-184

参考文献

[1] 张伟, 魏刚, 肖新科. 2A12铝合金本构关系和失效模型[J]. 兵工学报, 2013, 34(3):276-282.
ZHANG Wei, WEI Gang, XIAO Xin-ke. Constitutive relation and fracture criterion of 2A12 aluminum alloy [J]. Acta Armamentarii, 2013, 34(3): 276-282.
[2] Johnson G R, Cook W H. A constitutive model and data for metals subjected to large strains, high strain rates and high temperatures[C]. Proceedings of the seventh international symposium on ballistics, Hague, 1983, p.541.
[3] 杨明刚, 胡艳华, 余占军. 循环热处理超细38CrSi钢晶粒[J]. 金属热处理, 2015, 40(01):128-130.
YANG Minggang, HU Yanhua, YU Zhanjun. Grain ultra-refinement of 38CrSi steel with cyclic heat treatment[J]. Heat Treatment of Metals, 2015, 40(1)：128-130.
[4] 肖新科. 双层金属靶的抗侵彻性能和Taylor杆的变形与断裂[D]. 哈尔滨工业大学, 2010.
XIAO Xinke. The ballistic resistance of double-layered metallic target and the deformation & fracture of Taylor rod[D]. Harbin Institute of Technology, 2010.
[5] 张伟, 肖新科, 郭子涛, 等. 塑性功转热系数对钝头弹侵彻金属靶模拟结果的影响[J]. 兵工学报. 2010, 31(S1):167-171.
ZHANG Wei, XIAO Xinke, GUO Zitao, et al. Effect of plastic work-heat conversion rate on numerical prediction for metal target perforated by blunt projectile[J]. Acta Armamentarii, 2010, 31(S1)：167-171.
[6] 张伟, 肖新科, 郭子涛, 等. 双层A3钢靶对平头杆弹的抗侵彻性能研究[J]. 高压物理学报. 2012, 26(2):163-170.
ZHANG Wei, XIAO Xinke, GUO Zitao, et al. Investigation on the ballistic resistance of double-layered A3 steel target against blunt projectile impact[J]. Chinese Journal of High Pressure Physics, 2012, 26( 2)：163-170．
[7] Deng Y F, Zhang W, Cao Z S. Experimental investigation on the ballistic performance of 45 steel metal plates subjected to impact by hemispherical-nosed projectiles[J]. Chinese Journal of High Pressure Physics, 2013, 27(6):915-920.
[8] 邓云飞, 张伟, 曹宗胜, 等. 分层数对Q235钢薄板抗侵彻性能的影响[J]. 高压物理学报. 2013, 27(4):549-555.
DENG Yunfei, ZHANG Wei, CAO Zongsheng, et al. The influence of the number of layers on the ballistic resistance of layered thin A3 steel plates[J]. Chinese Journal of High Pressure Physics, 2013, 27(4)：549-555.
[9] 邓云飞, 张伟, 曹宗胜. 间隙对A3钢薄板抗卵形头弹侵彻性能影响的实验研究[J]. 振动与冲击. 2013, 32(12):95-99.
DENG Yunfei, ZHANG Wei, CAO Zongsheng. Effect of gap on behavior of a double-layered A3 steel shield against penetration of ogival rigid projectiles[J]. Journal of Vibration and Shock, 2013, 32(12)：95-99.
[10] 张伟, 魏刚, 肖新科, 等. 7A04高强铝合金抗杆弹正撞击性能实验研究[J]. 高压物理学报. 2011, 25(5):401-406.
ZHANG Wei, WEI Gang, XIAO Xinke. Experimental study on ballistic resistance property of 7A04 aluminum alloy against rod projectiles impact[J]. Chinese Journal of
[11] 邓云飞, 张伟, 孟凡柱, 等. Q235钢单层板对弹体抗撞击特性研究[J]. 机械工程学报, 2015, 51(7)：169-173.
DENG Yunfei, ZHANG Wei, MENG Fanzhu, et al. Investigation of the Ballistic Resistance of Q235 Steel Monolithic Targets[J]. Journal of Mechanical Engineering, 2015, 51(7)：169-173.
[12] Deng Y, Wei Z, Yang Y, et al. Experimental investigation on the ballistic performance of double-layered plates subjected to impact by projectile of high strength[J]. International Journal of Impact Engineering, 2014, 70(8):38-49.
[13] 邓云飞. 弹靶结构及其材料性能对金属靶抗侵彻特性影响研究[D]. 哈尔滨工业大学, 2012.
DENG Yun-fei. Research on the ballistic behavior of the monolithnic and multi-layered targets [D]. Harbin Institute of Technology, 2012.
[14] Xiao X, Zhang W, Wei G, et al. Effect of Projectile Hardness on Deformation and Fracture Behavior in the Taylor Impact Test[J]. Materials & Design. 2010, 31：4913-4920.
[15] Johnson G R, Cook W H. Fracture characteristics of three metals subjected to various strains, strain rates, temperatures and pressures[J]. Engineering Fracture Mechanics, 1985, 21(1):31-48.
[16] TENG X, WIERZBICKI T. Effect of fracture criteria on high velocity perforation of thin beams [J]. International Journal of Computational Methods, 2004, 1(01):171-200.
[17] Zhang W, Wei G, Xiao X K, et al. Effect of Fracture Criteria on Taylor Impact Fracture[J]. Journal of Harbin Institute of Technology, 2013, 20(1):63-67.
[18] 魏刚, 张伟, 邓云飞. 基于J-C模型的45钢本构参数识别及验证[J]. 振动与冲击, 已录用.
WEI Gang, ZHANG Wei, DENG Yunfei. Identification and Validation of Constitutive Model Parameters of 45 Steel Based on J-C Model[J]. Journal of Vibration and Shock, accetted.
[19] Børvik T, Hopperstad O S, Pedersen K O. Quasi-brittle fracture during structural impact of AA7075-T651 aluminium plates [J]. International Journal of Impact Engineering. 2010, 37(5): 537-551.
[20] Rakvåg K G, T. Børvik T, O. S. Hopperstad O S. A numerical study on the deformation and fracture modes of steel projectiles during Taylor bar impact tests [J]. International Journal of Solids and Structures. 2014, 51:808-821.
[21] Cockroft M G, Latham D J. Ductility and the Workability of Metals[J]. Journal of the Institute of Metals. 1968, 96:33-39.
[22] 朱耀, 庞宝君, 盖秉政. 一种用于动态拉伸试验装置的新型试件装卡方式[J]. 实验力学, 2009, 24(5)：433-438.
ZHU Yao, PANG Baojun, GAI Bingzheng. A new specimen fastener for dynamic tensile testing apparatus[J]. Journal of Experimental Mechanics, 2009, 24(5)：433-438.
[23] 张伟, 肖新科, 魏刚. 7A04铝合金的本构关系和失效模型[J]. 爆炸与冲击, 2011, 31(1):81-87.
ZHANG Wei, XIAO Xinke, WEI Gang. Constitutive relation and fracture criterion of 7A04 aluminum alloy [J]. Explosion and shock waves. 2011, 31(1):81-87.
[24] 郭子涛. 弹体入水特性及不同介质中金属靶的抗侵彻性能研究[D]. 哈尔滨工业大学, 博士学位论文. 2012.
GUO Zitao. Research on characteristics of projectile water entry and ballistic resistance of targets under different mediums[D]. Harbin Institute of Technology, 2012.