Ti/Cf/PEEK混杂层板低速冲击及剩余拉伸性能实验研究

PDF(1618 KB)

振动与冲击 ›› 2020, Vol. 39 ›› Issue (22) : 96-102.

论文

袁潇洒，Bhuwan Sapkota，郭华鑫，仲浪，潘蕾

作者信息 +

Experimental study on the low velocity impact damage and residual tensile properties of Ti/Cf/PEEK hybrid laminates

YUAN Xiaosa，Bhuwan Sapkota，GUO Huaxin，ZHONG Lang，PAN Lei

Author information +

文章历史 +

摘要

通过实验研究Ti/Cf/PEEK纤维金属层板低速冲击损伤机制及冲击后拉伸性能。混杂层板采用2/1和3/2两种铺层结构，铺层角度均为0°、45°、90°，分别在15J和25J冲击能量下进行冲击试验，对比分析两种铺层结构之间及同一铺层结构不同铺层角度之间的冲击损伤机制和剩余拉伸强度退化规律、剩余拉伸失效模式。结果表明：两种铺层结构的混杂层板冲击损伤机制主要有塑性变形、缩进、形成损伤区域、开裂、基质侵入金属损伤区域、纤维断裂、分层等，45°铺层角度的层板表现出较好的抗冲击损伤扩展性能。剩余拉伸强度退化规律与纤维铺放角度有关，0°铺放角度的层板冲击后剩余拉伸强度最高，其次是45°铺层方向，最差是90°铺层方向；2/1结构混杂层板剩余拉伸失效模式近似脆性断裂，而3/2结构层板既有延性断裂的特征，又有脆性断裂的特征。

Abstract

The low velocity impact damage mechanism and tensile properties after impact of Ti/Cf/PEEK fiber metal laminates were studied experimentally.The hybrid laminates were composed of 2/1 and 3/2 ply structures, and the ply angles of the both structures were 0°, 45°, 90°.The impact tests were carried out under the impact energy of 15 J and 25 J respectively.For the two types of ply structures and for the same structure with different ply angles, the impact damage mechanism, residual tensile strength degradation and residual tensile failure mode were compared and analyzed.The results show that the impact damage mechanism of the hybrid laminates with two kinds of ply structures mainly includes the processes of plastic deformation, indentation, formation of damaged areas, cracking, matrix erosion, fiber breakage, delamination, etc..45° layup direction laminates exhibit good impact damage resistance.The residual tensile strength degradation is related to the fiber placement angle.With 0° layup direction the remaining tensile strength of the laminates after impact is the highest, followed by the case of 45°layup direction, the worst is the case of 90°layup direction.The residual tensile failure mode of the 2/1 structural hybrid laminates is approximately brittle fracture, and that of the 3/2 structural laminates has both ductile fracture characteristics and brittle fracture characteristics.

导出引用

袁潇洒，Bhuwan Sapkota，郭华鑫，仲浪，潘蕾. Ti/Cf/PEEK混杂层板低速冲击及剩余拉伸性能实验研究[J]. 振动与冲击, 2020, 39(22): 96-102

YUAN Xiaosa，Bhuwan Sapkota，GUO Huaxin，ZHONG Lang，PAN Lei. Experimental study on the low velocity impact damage and residual tensile properties of Ti/Cf/PEEK hybrid laminates[J]. Journal of Vibration and Shock, 2020, 39(22): 96-102

参考文献

[1] Gin Boay Chai, Periyasamy Manikandan. Low velocity impact response of fibre-metal laminates – A review[J]. Composite Structures.2014, 107:363-381.
[2]陶杰,李华冠,潘蕾,胡玉冰.纤维金属层板的研究与发展趋势[J].南京航空航天大学学报,2015,47(05):626-636.
[2] Tao Jie, Li Huaguan, Pan Lei, Hu Yubing. Research and development trend of fiber metal laminates [J]. Journal of Nanjing University of Aeronautics and Astronautics, 2015, 47 (05): 626-636.
[3]吴志恩.纤维金属层板在飞机制造中的应用及工艺性分析[J].航空制造技术,2013(Z1):137-139.
[3] Wu Zhien. Application and Process Analysis of Fiber Metal Laminates in Aircraft Manufacturing[J]. Aviation Manufacturing Technology, 2013(Z1): 137-139.
[4]郑翔,童小燕,程起有,李斌,陈刘定.复合材料低速冲击及剩余压缩强度实验研究[J].机械科学与技术,2010,29(11):1574-1577.
[4] Zheng Xiang, Tong Xiaoyan, Cheng Qiyou, Li Bin, Chen Liuding.Experimental Study on Low Velocity Impact and Residual Compressive Strength of Composite Materials[J].Mechanical Science and Technology,2010,29(11):1574-1577.
[5] J.G.Carrillo, N.G.Gonzalez-Canche, E.A.Flores-Johnson, P.Cortes. Low velocity impact response of fibre metal laminates based on aramid fibre reinforced polypropylene[J]. Composite Structures.2019,220:708-716.
[6] Mohamed Habibi, Luc Laperrière, Hojjat Mahi Hassanabadi. Influence of low-velocity impact on residual tensile properties of nonwoven flax/epoxy composite[J].
Composite Structures.2018,186:175-182.
[7] Jarosław Bieniaś, Patryk Jakubczak. Impact damage growth in carbon fibre aluminium laminates[J]. Composite Structures.2017,172: 147-154.
[8] E.Cestino, G.Romeo, P.Piana, F.Danzi. Numerical/experimental evaluation of buckling behaviour and residual tensile strength of composite aerospace structures after low velocity impact[J]. Aerospace Science and Technology.2016,54:1-9.
[9] 陈勇,庞宝君,郑伟,刘源.玻璃纤维增强铝合金层板低速冲击力学特性及低温影响研究[J].振动与冲击,2014,33(17):203-208.
[9] Chen Yong, Pang Baojun, Zheng Wei, Liu Yuan. Study on low-speed impact mechanical properties and low temperature effects of glass fiber reinforced aluminum alloy laminates[J].Journal of Vibration and Shock,2014,33(17):203-208.
[10] 邓立伟,陈新文,王海鹏,罗舒.复合材料层合板低速冲击后的力学性能试验研究[J].纤维复合材料,2013,30(03):17-20.
[10] Deng Liwei, Chen Xinwen, Wang Haipeng, Luo Shu. Experimental study on mechanical properties of composite laminates after low velocity impact[J].Fiber Composites,2013,30(03):17-20.
[11] 姜舜,赵耀.纤维金属混杂层合板拉伸强度分析[J].舰船科学技术，2011,33（05）:33-37.
[11] Jiang Shun, Zhao Yao. Analysis of Tensile Strength of Fiber-Metal Hybrid Laminates[J]. Ship Science and Technology, 2011,33(05):33-37.
[12]程小全,康炘蒙,邹健,俞彬彬,郦正能.平面编织复合材料层合板低速冲击后的拉伸性能[J].复合材料学报,2008(05):163-168.
[12]Cheng Xiaoquan, Kang Yimeng, Zou Jian, Yu Binbin, Li Zhengneng. Tensile properties of flat braided composite laminates after low velocity impact[J]. Journal of Composite Materials, 2008(05):163-168.
[13]毛春见,许希武,郑达.缝合复合材料层板低速冲击及冲击后压缩实验研究[J].复合材料学报,2012,29(02):160-166.
[13]Mao Chunjian, Xu Xiwu, Zheng Da.Experimental study on low velocity impact and post-impact compression of stitched composite laminates[J].Journal of Composite Materials,2012,29(02):160-166.
[14]徐凤娟. Ti/APC-2复合层板基本力学性能的有限元模拟研究[D].南京航空航天大学,2013.
[14]Xu Fengjuan. Finite element simulation of basic mechanical properties of Ti/APC-2 composite laminates [D]. Nanjing University of Aeronautics and Astronautics, 2013.