含圆孔缺陷三点弯曲梁的裂纹扩展特性实验研究

PDF(3153 KB)

振动与冲击 ›› 2020, Vol. 39 ›› Issue (5) : 74-80.

论文

梅比

作者信息 +

Tests for crack propagation characteristics of three-point bending beam with circular hole defect

MEI Bi

Author information +

文章历史 +

摘要

采用动态焦散线实验系统，对含圆孔缺陷的PMMA材料进行冲击断裂力学实验，研究三点弯曲梁中不同直径和位置的圆孔缺陷对扩展裂纹的影响。实验结果表明：扩展裂纹与圆孔缺陷相互作用前，呈现Ⅰ型拉伸断裂，扩展路径平直；与圆孔缺陷相互作用后，贯通萌生的次裂纹沿直线继续扩展，未贯通的裂纹偏移扩展。扩展裂纹与路径上圆孔缺陷贯通过程中，裂纹扩展速度和动态应力强度因子快速降为零，裂纹的扩展受到抑制，且圆孔直径越大、距离越近，抑制作用越显著；贯通萌生次生裂纹的起裂速度和起裂韧度，随着圆孔缺陷直径的增大而变大。扩展裂纹与偏置圆孔缺陷相互作用过程中，当圆孔缺陷直径越大、偏置距离越小，裂纹起偏距离越短，最大偏移量越大，并且扩展裂纹动态应力强度因子和扩展速度局部小幅增大。研究结果为分析动态裂纹扩展特征和材料破坏模式提供借鉴。

Abstract

Effects of circular hole defect with different diameters and positions on crack propagation characteristics was tested and studied for a 3-point bending beam with this hole defect made of PMMA material subjected to impact load using a dynamic caustic line test system.The results showed that before propagating crack interacts with circular hole defect, crack propagation reveals I type tensile fracture, and propagation path is straight; after propagating crack interacts with circular hole defect, penetrated initiating secondary crack continues to propagate in a straight line, and unpenetrated crack propagates in offset; in process of crack propagation penetrating circular hole defect, crack propagation velocity and dynamic stress intensity factor (DSIF) drops rapidly to zero, crack propagation is suppressed, the larger the hole diameter and the nearer the distance to hole, the more significant the suppression action; both initial speed and initial fracture toughness of penetrated initiating secondary crack increase with increase in circular hole defect diameter; in process of interaction between propagating crack and offset circular hole defect, the larger the hole diameter and the smaller the offset distance, the shorter the initial offset distance of crack and the larger the maximum offset, and DSIF and propagation velocity of crack propagation increase a little bit locally; the study results provide a reference for analyzing dynamic crack propagation features and material failure mode.

导出引用

梅比. 含圆孔缺陷三点弯曲梁的裂纹扩展特性实验研究[J]. 振动与冲击, 2020, 39(5): 74-80

MEI Bi. Tests for crack propagation characteristics of three-point bending beam with circular hole defect[J]. Journal of Vibration and Shock, 2020, 39(5): 74-80

参考文献

[1] YANG R S，XU P，YUE Z W，et al. Dynamic fracture analysis of crack–defect interaction for mode I running crack using digital dynamic caustics method[J]. Engineering Fracture Mechanics，2016，161：63-75.
[2] 李地元，成腾蛟，周韬，等. 冲击载荷作用下含孔洞大理岩动态力学破坏特性试验研究[J]. 岩石力学与工程学报，2015，34（2）：249-260.
LI Diyuan，CHENG Tengjiao，ZHOU Tao，et al. Experimental study of the dynamic strength and fracturing characteristics of marble specimen with a single hole under impact loading[J]. Chinese Journal of Rock Mechanics and Engineering，2015，34（2）：249-260.
[3] 杨圣奇，吕朝辉，渠涛. 含单个孔洞大理岩裂纹扩展细观试验和模拟[J]. 中国矿业大学学报，2009，38（6）：774-781.
YANG Shengqi，LU Chaohui，QU Tao. Investigations of crack expansion in marble having a single pre-existing hole: Experiment and Simulations[J]. Journal of China University of Mining & Technology，2009，38（6）：774-781.
[4] 左建平，黄亚明，刘连峰. 含偏置缺口玄武岩原位三点弯曲细观断裂研究[J]. 岩石力学与工程学报，2013，32（4）：740-746.
ZUO Jianping，HUANG Yaming，LIU Lianfeng. Investigation on meso-fracture mechanism of basalt with offset notch based on in-situ three-point bending tests[J]. Chinese Journal of Rock Mechanics and Engineering，2013，32（4）：740-746.
[5] 李清，薛耀东，于强，等. 含预制裂纹的悬臂梁－柱试件冲击断裂实验[J]. 矿业科学学报，2018，3(2):139－147.
LI Qing，XUE Yaodong，YU Qiang，et al. Experimental study on impact fracture of cantilever beam-column specimen with prefabricated crack[J]． Journal
of Mining Science and Technology，2018，3( 2):139－147.
[6] SHCHERBAKOV I P，KUKSENKO V S，CHMEL A E. Size, location and time of initiation of primary defects in rocks under impact destruction[J]. Journal of Mining Science，2017，53（1）：197-200.
[7] WANG Y B，YANG R S，ZHAO G F. Influence of empty hole on crack running in PMMA plate under dynamic loading[J]. Polymer Testing, 2017, 58:70-85.
[8] SAADATI M，FORQUIN P，WEDDFELT K，et al. On the mechanical behavior of granite material with particular emphasis on the influence from pre-existing cracks and defects[J]. Journal of Testing and Evaluation，2018，46（1）：33-45.
[9] JELAGIN D，SAADATI M，JERJEN, I，et al. Mechanical Characterization of Granite Rock Materials: On the Influence from Pre-Existing Defects[J]. Journal of Testing and Evaluation，2018，46（2）：540-548.
[10] 程龙，杨圣奇，刘相如. 含缺陷砂岩裂纹扩展特征试验与模拟研究[J]. 采矿与安全工程学报，2012，29（5）：719-724.
CHENG Long，YANG Shengqi，LIU Xiangru. Experimental and Numerial Investigation on Crack Expansion of Sandstone Containing Flaws[J]. Journal of Mining & Safety Engineering，2012，29（5）：719-724.
[11]刘瑞峰，朱哲明，李盟，等.爆炸载荷下Ⅰ型裂纹的起裂及扩展规律研究[J].岩石力学与工程学报，2018，37(02)：392-402.
LIU Ruifeng，ZHU Zheming，LI Meng，et al. Study on Initiation and Propagation of Mode I Crack under Blasting[J]. Chinese Journal of Rock Mechanics and Engineering，2018，37(02)：392-402.
[12] 高桂云，周洁，励争. 脆性材料裂纹与损伤相互作用的试验研究[J].岩石力学与工程学报，2017，36(11)：2650-2661.
GAO Guiyun，ZHOU Jie，LI Zheng. Experimental study on the interaction of crack and defects of brittle materials under dynamic loading[J]. Chinese Journal of Rock Mechanics and Engineering，2017，36（11）：2650-2661.
[13] 李盟，朱哲明，肖定军，等．煤矿岩巷爆破掘进过程中周边眼对裂纹扩展止裂机理[J]．煤炭学报，2017，42(7)：1691-1699.
LI Meng，ZHU Zheming，XIAO Dingjun， et al．Mechanism of crack arrest by peripheral holes during mine rock roadway excavation under blasting[J]．Journal of China Coal Society，2017，42(7)：1691-1699.
[14] 杨永明，鞠杨，陈佳亮. 劈裂荷载下孔隙岩石应力分布特征与裂纹扩展行为[J]．煤炭学报，2014，39 (4)：658-665.
YANG Yongming，JU Yang，CHEN Jialiang. Distribution properties of stress and cracks propagation behavior of porous rocks during splitting[J]． Journal of China Coal Society，2014，39( 4)：658-665.
[15] KALTHOFF J F. The shadow optical method of caustics [M]. Static and Dynamic Photo-elasticity and Caustics. Springer Vienna, 1987:407-522.
[16] PAPADOPOULOS G A. Fracture mechanics：the experimental method of caustics and the det.-criterion of fracture[M]. London：Springer- Verlag London Limited，1993：211-220.
[17] ROSSMANITH H P, DAEHNKE A, NASMILLNER R E K, et al. Fracture mechanics applications to drilling and blasting [J]. Fatigue & Fracture of Engineering Materials & Structures, 1997, 20(11): 1617-1636.
[18] 李清. 爆炸致裂的岩石动态力学行为与断裂控制试验研究[博士学位论文][D]. 北京：中国矿业大学(北京)，2009.
LI Qing. Experiment of fracture behaviors and control for crack propagation under blasting load[Ph. D. Thesis][D]. Beijing：China University of Mining and Technology，2009.
[19] 杨立云，张勇进，孙金超，等.偏置裂纹对含双裂纹PMMA试件动态断裂影响效应研究[J].矿业科学学报，2017，2(04)：330-335.
YANG Liyun，ZHANG Yongjin，SUN Jinchao，et al. The effect of offset distance on dynamic fracture behavior of PMMA with double cracks[J] Journal of Mining Science and Technology，2017，2(4):330－335.
[20] 郭东明，闫鹏洋，薛磊，等. 动静载荷下巷道围岩裂纹扩展规律的试验研究[J].矿业科学学报，2016，1(02)：146-154.
GUO Dongming, YAN Pengyang, XUE Lei，et al. The experimental research on the propagation laws of cracks in roadway surrounding rock subjected to static-dynamic load[J]. Journal of Mining Science and Technology，2016，1(2)：146-154.
[21] 岳中文，宋耀，邱鹏，等. 冲击载荷下双预置裂纹三点弯曲梁动态断裂实验[J]. 振动与冲击, 2017, 36(4): 151-156.
YUE Zhongwen， SONG Yao， QIU Peng，et al. A dynamic fracture experiment of a three-point-bend beam containing double pre-existing cracks under impact load[J]. Journal of Vibration and Shock，2017，36(4)：151-156.
[22] 杨仁树，许鹏，岳中文，等. 圆孔缺陷与I型运动裂纹相互作用的试验研究[J]. 岩土力学，2016，37(6)：1597-1603.
YANG Renshu，XU Peng，YUE Zhongwen，et al. Laboratory study of interaction between a circular hole defect and modeⅠ moving crack[J]. Rock and Soil Mechanics，2016，37(6)：1597-1603.