A study on fracture fractal of high temperature spray cooled carbon nanotube concrete under impact load

TIAN Wei，GAO Fangfang

Author information +

文章历史 +

摘要

在混凝土中掺入具有高强、高韧和良好热导性的多壁碳纳米管（multi walled carbon nanotubes ,MWCNTs）对普通混凝土的耐高温性能进行了增强，并以分形维数为指标研究了高温喷淋冷却后碳纳米管增强混凝土在冲击荷载作用下的分形特征和能耗特性，建立了分形维数与动强度、能耗及冲击韧性之间的关系。研究结果表明，高温喷淋冷却后的混凝土在冲击载荷下，其冲击破碎块的分形维数随应变速率和温度的增大而增大；在同一温度下，混凝土的动态抗压强度、能耗和冲击韧性随着分形维数的增加而增加；在同一冲击气压下，混凝土的动态抗压强度、能耗和冲击韧性随着分形维数的增加而减小；相比而言，添加了碳纳米管后混凝土高温喷淋冷却后在冲击荷载下的破裂程度得到有效缓解，其分形维数减小，能耗、冲击韧性和动强度都得到明显提高。

Abstract

In order to improve the impact resistance of concrete after high temperature, multi walled carbon nanotubes (MWCNTs) with high strength, high toughness and good thermal conductivity are added into the concrete. And the fractal characteristics and energy consumption characteristics of carbon nanotube reinforced concrete under impact loading after high temperature are explored by the fractal index (i.e. fractal dimension), and the relationship between fractal dimension and dynamic compressive strength, energy consumption and impact toughness is established. The results show that after high temperature, the fractal dimension of concrete impact fracture increases with the increase of strain rate and temperature under impact load. At the constant temperature, the dynamic compressive strength, energy consumption and impact toughness of concrete increase with the increase of fractal dimension, while at the constant impact pressure, the they perform the opposite trend. Meanwhile, compared with ordinary plain concrete, concrete incorporating with multi walled carbon nanotubes owns light crushing degree, small fractal dimension, high energy consumption, impact toughness and dynamic compressive strength. In fact, the variation of fractal dimension essentially depends on the compactness of concrete and the propagation degree of internal crack. Well dispersed multi walled carbon nanotubes in concrete could not only refine pores, but also provide attachment points for hydration products and promote hydration process, so as to improve the compactness of concrete matrix. Besides, the bridging, pullout and thermal conductivity of multi walled carbon nanotube are also conducive to inhibit and delay the initiation and propagation of temperature cracks and load cracks. Consequently, the resistance of concrete with multi walled carbon nanotubes to high temperature and impact load has been effectively improved.

导出引用

田威，高芳芳. 冲击荷载下高温喷淋冷却碳纳米管混凝土破裂分形研究[J]. 振动与冲击, 2023, 42(4): 70-80

TIAN Wei，GAO Fangfang. A study on fracture fractal of high temperature spray cooled carbon nanotube concrete under impact load[J]. Journal of Vibration and Shock, 2023, 42(4): 70-80

参考文献

[1] Iijima S. Helical microtubules of graphitic carbon[J]. Nature, 1991, 354(6348): 56-58.
[2] Reich, S., Thomsen C., & Maultzsch J. Carbon Nanotubes: Basic Concepts and Physical Properties[M], WILEY-VCH Verlag GmbH & Co.KGaA, 2007.
[3] Konsta-Gdoutos M. S., Metaxa Z. S., & Shah, S. P. Multi-scale mechanical and fracture characteristics and early-age strain capacity of high performance carbon nanotube/cement nanocomposites[J]. Cement and Concrete Composites, 2010, 32(2): 110-115.
[4] Xu S. L., Liu J. T., & Li Q. H. Mechanical properties and microstructure of multi-walled carbon nanotube-reinforced cement paste[J]. Construction and Building Materials, 2015, 76: 16-23.
[5] Isfahani F. T., Li W., & Redaelli E. Dispersion of multi-walled carbon nanotubes and its effects on the properties of cement composites[J]. Cement and Concrete Composites, 2016, 74: 154-163.
[6] Mohsen M. O., Taha R., Taqa A. A., & Shaat A. Optimum carbon nanotubes’ content for improving flexural and compressive strength of cement paste[J]. Construction and Building Materials, 2017, 150: 395-403.
[7] Gao F. F., Tian W., Wang Z., et al. Effect of diameter of multi-walled carbon nanotubes on mechanical properties and microstructure of the cement-based materials[J]. Construction and Building Materials, 2020, 260: 120452.
[8] Pop E., Mann D., Wang Q., et al. Thermal Conductance of an Individual Single-Wall Carbon Nanotube above Room Temperature, Nano Letters, 2006, 6(1): 96-100.
[9] Yu Z., & Lau D. Evaluation on mechanical enhancement and fire resistance of carbon nanotube (CNT) reinforced concrete[J]. Coupled Systems Mechanics, 2017, 6(3): 335-349.
[10] Gao F. F., Tian W., Wang Y. W., et al. Effect of the dosage of MWCNTs on deterioration resistant of concrete subjected to combined freeze-thaw cycles and sulfate attack[J]. Structural Concrete, 2020, (6): E955-E965.
[11] Gao F. F., Tian W., Cheng X. Investigation of moisture migration of MWCNTs concrete after different heating-cooling process by LF-NMR[J]. Construction and Building Materials, 2021, 288(11): 123146.
[12] Baloch, W. L., Khushnood, R. A., & Khaliq, W. Influence of multi-walled carbon nanotubes on the residual performance of concrete exposed to high temperatures[J]. Construction and Building Materials, 2018, 185: 44-56.
[13] Pawel S., Mohamed A. E., Cendrowski S. Y. C., et al. Mechanical and microstructural properties of cement pastes containing carbon nanotubes and carbon nanotube-silica core-shell structures, exposed to elevated temperature[J]. Cement and Concrete Composites, 2019, 95: 193-204.
[14] Sedaghatdoost A., & Behfarnia K. Mechanical properties of Portland cement mortar containing multi-walled carbon nanotubes at elevated temperatures[J]. Construction and Building Materials, 2018, 176(7): 482-489.
[15] Liu S, Zhu D. Y., Ou Y. F., et al. Impact response of basalt textile reinforced concrete subjected to different velocities and temperatures[J]. Construction and Building Materials, 2018, 175(JUN.30): 381-391.
[16] 任韦波, 许金余, 刘远飞, 等. 高温后玄武岩纤维混凝土冲击破碎分形特征[J].振动与冲击, 2014, 33(10): 167-171+188. (Ren Weibo, Xu Jinyu, Liu Yuanfei, et al. Fractal characteristics of fragments of basalt fiber reinforced concrete after elevated temperatures under impact loading[J]. Journal of Vibration and Shock, 2014, 33(10): 167-171+188.)
[17] 施劲松, 许金余, 任韦波, 等. 高温后混凝土冲击破碎能耗及分形特征研究[J]. 兵工学报, 2014, 35(05): 703-710. (Ren Weibo, Xu Jinyu, Liu Yuanfei, et al. Research on energy dissipation and fractal characteristics of concrete after exposure to elevated temperatures under impact loading[J]. Acta Arm Mmentarii, 2014, 35(05): 703-710.)
[18] 曹茂森, 任青文, 翟爱良, 等. 混凝土结构损伤的分形特征实验分析[J]. 岩土力学, 2005(10): 49-53. (Cao Maosen, Ren Qingwen, Qu Ailiang, et al. Experimental study on fractal characterization in damages of concrete structures[J]. Rock and Soil Mechanics, 2005(10): 49-53.)
[19] Ochiai M., Ozao R., Yamazaki Y., et al. Self-similarity law of particle size distribution and energy law in size reduction of solids[J]. Physica A: Statistical Mechanics and its Applications, 1992, 191(1): 295-300.
[20] Turcotte D. L. Fractals and fragmentation[J]. Journal of Geophysical Research-Solid Earth, 1986, 91(B2): 1921-1926.
[21] Borodich F. M. Fractals and fractal scaling in fracture mechanics[J]. International Journal of Fracture, 1999, 95(1-4): 239-259.
[22] Grote D. L., Park S. W., & Zhou M. Dynamic behavior of concrete at high strain rates and pressures: I. Experimental characterization[J]. International Journal of Impact Engineering, 2001, 25(9): 869-886.
[23] Hild F. On characteristic parameters involved in dynamic fragmentation processes[J]. Mechanics of Materials, 2015, 80: 340-350.
[24] Yan A., Wu K. R., Zhang D., et al. Effect of fracture path on the fracture energy of high-strength concrete[J]. Cement and Concrete Research, 2001, 31(11): 1601-1606.
[25] Gray G. Classic Split-Hopkinson pressure bar testing[M]. ASM Handbook, Mechanical Testing and Evaluation, 2000, 8: 462-476:
[26] Ramesh K. T. High rates and impact experiments[M]. Springer US, 2008.
[27] GB/T50081-2002, 普通混凝土力学性能试验方法标准[S]. 北京:中国建筑工业出版社, 2003. (GB/T50081-2002, Standard for test method of mechanical properties on ordinary concrete[S]. Beijing: China Architecture Press, 2003.)
[28] Poon, C. S., Azhar S., Anson M., et al. Strength and durability recovery of fire-damaged concrete after post-fire-curing[J]. Cement and Concrete Research, 2001, 31: 1307-1318.
[29] Suh H., Jee H., Kim J., et al. Influences of rehydration conditions on the mechanical and atomic structural recovery characteristics of Portland cement paste exposed to elevated temperatures[J]. Construction and Building Materials, 2020, 235: 117453.
[30] Bangi M. R., Horiguchi T. Pore pressure development in hybrid fibre-reinforced high strength concrete at elevated temperatures[J]. Cement and Concrete Research, 2011, 41(11): 1150-1156.
[31] Ren W. B., & Xu J. Y. Fractal Characteristics of Concrete Fragmentation under Impact Loading[J]. Journal of Materials in Civil Engineering, 2016, 29(4): 04016244.
[32] 易顺民, 唐辉明. 三轴压缩条件下三峡坝基岩石破裂的分形特征[J]. 岩土力学, 1999, 4(03): 24-28. (Yi Shunming, Tang Huiming. The fractal characteristics of fracture of dam foundation rock under under triaxial compression in three gorges project[J]. Rock and soil mechanics, 1999, 4(03): 24-28.)
[33] Xie H. Response to discussion on the fractal effect of irrergularity of crack branching on the fracture toughness of brittle materials[J]. International Journal of Fracture, 1994: 65(4): R71-R75.
[34] 田威. 混凝土损伤演化的研究及其在细观数值模拟中的应用[D]. 博士论文. 西安理工大学, 2009. (Tian wei. CT study on the concrete-damage evolution and its application in numerical stimulation[D]. Doctoral thesis, Xi'an University of Technology, 2009.)
[35] 黄达, 谭清, 黄润秋. 高围压卸荷条件下大理岩破碎块度分形特征及其及能量相关性研究[J]. 岩石力学与工程学报, 2012, 31(7): 1379-1389. (Hung Da, Tan Qing, Huang Runqiu. Fractal characteristics of fragmentation and correlation with energy of marble under unloading with high confining pressure[J]. Chinese journal of rock mechanics and Engineering, 2012, 31(7): 1379-1389.)
[36] Liang W. B., Zhao J. H., Li Y., et al. Research on the Fractal Characteristics and Energy Dissipation of Basalt Fiber Reinforced Concrete after Exposure to Elevated Temperatures under Impact Loading[J]. Materials, 2020, 13(8): 1902.
[37] Zhang Z. X., Kou S. Q., Jiang L. G., et al. Effects of loading rate on rock fracture: fracture characteristics and energy partitioning[J]. International Journal of Rock Mechanics and Mining Sciences, 2000, 37(5): 745-762.