Vulnerability of building laminated glass against wind-induced projectiles impact

PDF(5203 KB)

Journal of Vibration and Shock ›› 2024, Vol. 43 ›› Issue (9) : 267-275.

ZHANG Yong, LI Shouke, GUO Fan, LEI Jiayan, PENG Xiong, SUN Hongxin, LIU Min

Author information +

History +

Abstract

The finite element simulation method is used to study the impact vulnerability of building laminated glasses for windborne debris. The finite element model of laminated glass impacted by windborne debris is established with LS-DYNA, and the reliability of the finite element model is verified by comparative experiments and numerical simulation results. The crack development and stress propagation of laminated glass impacting by spherical windborne debris are analyzed. By changing the impact position and the aspect ratio of the laminated glass panel, as well as with different radius and material of windborne debris, the impact effects on the laminated glass are studied. The impact failure probability of the laminated glass is calculated by using the two-parameter Weibull distribution. It is shown that, compared impact location with the middle and edge of laminated glass, the impact resistance with corner impact is the worst; at the same impact velocity, the failure probability of laminated glass increases with the increasement of windborne debris radius; compared with stone debris and wood debris, the critical impact damage velocity is the lowest when steel debris impact laminated glass; as the panel area is constant, the failure probability decreases firstly and then increases with increasement of aspect ratio.

Key words

windborne debris / laminated glass / numerical simulation / failure probability

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations

ZHANG Yong, LI Shouke, GUO Fan, LEI Jiayan, PENG Xiong, SUN Hongxin, LIU Min. Vulnerability of building laminated glass against wind-induced projectiles impact[J]. Journal of Vibration and Shock, 2024, 43(9): 267-275

References

[1] 宿海良，东高红，王猛，等. 1949年-2018年登陆台风的主要特征及灾害成因分析研究[J]. 环境科学与管理, 2020, 45(05): 128-131. Su Hailiang, Dong Gaohong, Wang Meng, et al. Analysis on Main Characteristics and Causes of Landfall Typhoons in Recent 70 Years[J]. Environmental science and management, 2020, 45(05): 128-131. [2] HOLMES J D. Windborne debris and damage risk models: a review[J]. Wind & Structures An International Journal, 2010, 13(13) : 54-66. [3] LIN N, VANMARCKE E. Windborne debris risk analysis: part I: introduction and methodology[ J]. Wind and Structures, 2010, 13(2): 191-206 [4] MCDONALD J R, MEHTA K C, MINOR J E. Tornado-resistant design of nuclear power-plant structures[J]. Nucl. Saf. 1974, 15: 432–439. [5] WILLS J A B, LEE B E, WYATT T A. A Model of Wind-Borne Debris Damage[J].Journal of Wind Engineering and Industrial Aerodynamics, 2002, 90（4-5）：555–565. [6] TACHIKAWA M. Trajectories of flat plates in uniform flow with application to wind-generated missiles[J]. Journal of Wind Engineering & Industrial Aerodynamics, 1983, 14(1-3): 443-453. [7] HOLMES J D, BAKER C J,TAMURA Y. Tachikawa Number: A Proposal[J].Journal of Wind Engineering and Industrial Aerodynamics, 2006, 94(1):41-47. [8] KAKIMPA B, HARGREAVES D M, OWEN J S, et al. CFD modelling of free-flight and auto-rotation of plate type debris[J]. Wind & Structures An International Journal, 2010, 13(2): 1089-93. [9] 朱晓洁. 棒状飞射物飞行特性的数值模拟 [D].哈尔滨；哈尔滨工业大学,2007. [10] 莫红涛. 板状飞射物与风场耦合飞行行为的数值模拟[D]. 哈尔滨；哈尔滨工业大学,2012. [11] 尹亮. 板状飞射物飞行特性的非定常CFD数值模拟[D]. 哈尔滨；哈尔滨工业大学,2020 [12] ZHANG X H, HAO H, MA G W. Laboratory test and numerical simulation of laminated glass window vulnerability to debris impact[J]. International Journal of Impact Engineering, 2013, 55: 49-62. [13] 张文娜,钱江.核电站特种气密防火门在风致飞射物冲击作用下安全性能研究[J].振动与冲击,2017,36(05):221-226+245. ZHANG Wenna, QIAN Jiang. Safety performance of a special airtight anti-fire door for nuclear power station subjected to windborne debris impact[J]. Journal of Vibration and Shock, 2017,36(05):221-226+245. [14] 陈胜,黄鹏,顾明.风致飞掷物冲击建筑浮法玻璃试验和数值模拟[J]. 振动与冲击,2022,41(01):24-30. CHEN Sheng, HUANG Peng, GU Ming. Tests and numerical simulation of wind-induced flying projectile impacting building float glass[J]. Journal of Vibration and Shock, 2022,41(01):24-30. [15] CHEN S, ZANG M, WANG D,et al. Finite element modelling of impact damage in polyvinyl butyral laminated glass[J]. Composite Structures, 2016, 138, 1-11. [16] WANG X, YANG J, LIU Q,et al.A comparative study of numerical modelling techniques for the fracture of brittle materials with specific reference to glass[J]. Engineering Structures, 2017,152, 493-505. [17] WANG X, YANG J, WANG F,et al. Simulating the impact damage of laminated glass considering mixed mode delamination using FEM/DEM[J]. Composite Structures, 2018,202, 1239-1252. [18] GAO W, XIANG J, CHEN S, et al. Intrinsic cohesive modeling of impact fracture behavior of laminated glass[J]. Materials & Design, 2017, 127, 321-335. [19] CHEN X, CHAN A H C. Modelling impact fracture and fragmentation of laminated glass using the combined finite-discrete element method[J]. International Journal of Impact Engineering, 2018, 112, 15-29. [20] CHEN X, CHAN A. Soft impact responses of laminated glass simulated with the combined finite-discrete element method[J]. Engineering Computations, 2018, 35(3), 1460-1480. [21] CHEN X, CHEN X, CHAN A H C, et al.. Parametric analyses on the impact fracture of laminated glass using the combined finite-discrete element method[J]. Composite Structures, 2022, 297, 115914. [22] WANG Z, MA D, SUO T, et al. Investigation into different numerical methods in predicting the response of aluminosilicate glass under quasi-static and impact loading conditions[J]. International Journal of Mechanical Sciences, 2021, 196, 106286. [23] LEI Z, ROUGIER E, KNIGHT E E, et al. Impact fracture and fragmentation of glass via the 3D combined finite-discrete element method[J]. Applied Sciences, 2021, 11, 2484. [24] CHEN X, OU W, FUKUDA D, et al. Three-dimensional modelling on the impact fracture of glass using a GPGPU-parallelised FDEM[J]. Engineering Fracture Mechanics, 2023, 277, 108929. [25] 闫占乱. 汽车前风挡玻璃抗冲击与吸能性能仿真研究[D]. 武汉；武汉理工大学, 2021. [26] 陈星,陈素文,李国强. 爆炸作用下框支式聚乙烯醇缩丁醛夹层玻璃的破坏模式[J]. 同济大学学报（自然科学版）, 2021,49(11):1565-1574. CHEN Xing, CHEN Suwen, LI Guoqiang. Failure mode of framed polyvinyl butyral-laminated glass subjected to blast loading [J]. Journal of Tongji University (Natural Science), 2021,49(11):1565-1574. [27] HOLMQUIST T J, JOHNSON G R, LOPATIN C M, et a. High strain rate properties and constitutive modeling of glass[R]. Albuquerque: Sandia National Labs, 1995． [28] XU J,LI Y B,GE D Y. Experimental investigation on constitutive behavior of PVB under impact loading[J].International Journal of Impact Engineering,2011,38:106-114 [29] J. O. HALLQUIST, LS-DYNA keyword users manual, Livermore Software Technology Corporation[M].2012. [30] LANI L, FROLI M. Adhension,creep and relaxation properties of PVB in laminated safety glass[C]. GPD Finland. Proceedings of the glass performance days. Finland, Tampere; 2011,1-4. [31] GURVICH M R，DIBENEDETTO A T．Evaluation of the Statistical Parameters of a Weibull Distribution［J］.Journal of Materials Science,1997（32）:3711～3716. [32] BONA A D,ANUSAVICE K J，DeHoff PH. Weibull analysis and flexural strength of hot-pressed core and veneered ceramic structures. Dental Materials,2003,19(7):662-669.